The main two-component self-dry coating composition editor: Part B Paint: Central molecule epoxy resin, specialty resins, zinc powder, additives and diluents and other components. Another component: amine curing agent. 2 Key Features editor rich zinc, zinc electrochemical protection of the coating has a very prominent anti-corrosion properties. Film hardness. High temperature, does not affect the welding performance. Superior drying performance. High adhesion, good mechanical properties. 3 Technical Specifications edited film appearance film is smooth, color standard model drying time, the standard thickness of single coating, 25 ℃ table dry ≤2h, hard work ≤12h adhesion, Fones method, class ≤2 welding burn width ≤15mm Salt water, 3%, 168h does not blister, do not fall off, do not rust 4 Packing edit paint: 25kg / barrel H-100 hardener: 2.5kg / barrel 5 basic parameters edit ratio ︰ paint hardener 10︰ 1 (by weight) Paint density 2.38 Construction time 25 ℃, 8h theoretical amount 200 ~ 250g / m 6 recoat edit temperature Minimum Maximum 10 ℃ 48h 20d 25 ℃ 24h 15d 30 ℃ 16h 7d Note: When the maximum overcoating intervals or industrial atmosphere, maritime environment, zinc white paint surfaces may rust (zinc), if this happens, shall, before the finish after painting, using sweep blasting or with power tools, sandpaper and other coating surface treatment, divisible all zinc salts and dirt. 7 Curing time Curing time temperature 10 ℃ 40min 25 ℃ 30min 30 ℃ 15min 8 painting number for shop primers, coating a dry film thickness of 25 ± 5mm for anti-rust primer, dry film thickness of 55 ± 5mm 9 support aluminum tripolyphosphate rust epoxy paint H53-33 H53-89 epoxy micaceous iron oxide intermediate layer paint S04-16 metal corrosion epoxy paint finish H04-18 JX04-28 neoprene corrosion paint B04-10 10 surface treatment acrylic polyurethane enamel paint base to clean, free of all dirt grease, dust, etc. Sand blasting or shot blasting to reach Sweden Sa2.5 level, manual mechanical descaling reach St2-3 level. 11 airless spray coating method: Thinner: X-17 epoxy diluent: 0 to 15% (by weight paint) Nozzle diameter: about 0.4 ~ 0.5mm ejection pressure: 15 ~ 20MPa Air Spray: Thinner: X-17 epoxy diluent: 0 to 20% (by weight paint) Nozzle diameter: about 1.8 ~ 2.5mm ejection pressure: 0.3 ~ 0.5MPa Roller / Brush: Thinner: X -17 epoxy diluent: 0 to 20% (by weight paint) 12 shelf life Store in a cool, dry, well-ventilated place, paint a year, a curing agent for six months. 13 Note 1, read the instructions before construction. 2, before using the paint and hardener ratio adjusted as required, how much with how much stir used within 8 hours. 3, the construction process remains dry and clean. 4, with paint hardener drums must Gaiyan avoid gelling. 5, during construction and dry, relative humidity not greater than 85% shall be for one day after the delivery of the product to painting. 6, easy to form a zinc rich primer surface should not be prolonged exposure before the finish after painting. As long interval painting, recommended H53-89 epoxy micaceous iron oxide intermediate layer paint closed.